Predicting the fatigue life of solder interconnections is a challenge due to the complex nonlinear behavior of solder alloys and the importance of the load history. Long experience with Sn–Pb solder alloys together with empirical fatigue life models such as the Coffin–Manson rule have helped us identify reliable choices among package design alternatives. However, for the currently popular Pb-free choice of SnAgCu solder joints, designing accelerated thermal cycling tests and estimating the fatigue life are challenged by the significantly different creep behavior relative to Sn–Pb alloys. In this paper, a hybrid fatigue modeling approach inspired by nonlinear fracture mechanics is developed to predict the crack trajectory and fatigue life of a solder interconnection. The model is shown to be similar to well accepted cohesive zone models in its theoretical development and application and is anticipated to be computationally more efficient compared to cohesive zone models in a finite element setting. The approach goes beyond empirical modeling in accurately predicting crack trajectories and is validated against experiments performed on lead-free as well as Sn–Pb solder joint containing microelectronic packages. Material parameters relevant to the model are estimated via a coupled experimental and numerical technique.
Skip Nav Destination
e-mail: ganeshs@purdue.edu
Article navigation
June 2008
Research Papers
A Nonlinear Fracture Mechanics Approach to Modeling Fatigue Crack Growth in Solder Joints
D. Bhate,
D. Bhate
School of Mechanical Engineering,
Purdue University
, West Lafayette, IN 47907-2088
Search for other works by this author on:
D. Chan,
D. Chan
School of Mechanical Engineering,
Purdue University
, West Lafayette, IN 47907-2088
Search for other works by this author on:
G. Subbarayan,
G. Subbarayan
School of Mechanical Engineering,
e-mail: ganeshs@purdue.edu
Purdue University
, West Lafayette, IN 47907-2088
Search for other works by this author on:
L. Nguyen
L. Nguyen
National Semiconductor Corporation
, Santa Clara, CA 95051
Search for other works by this author on:
D. Bhate
School of Mechanical Engineering,
Purdue University
, West Lafayette, IN 47907-2088
D. Chan
School of Mechanical Engineering,
Purdue University
, West Lafayette, IN 47907-2088
G. Subbarayan
School of Mechanical Engineering,
Purdue University
, West Lafayette, IN 47907-2088e-mail: ganeshs@purdue.edu
L. Nguyen
National Semiconductor Corporation
, Santa Clara, CA 95051J. Electron. Packag. Jun 2008, 130(2): 021003 (9 pages)
Published Online: April 15, 2008
Article history
Received:
January 5, 2007
Revised:
August 20, 2007
Published:
April 15, 2008
Citation
Bhate, D., Chan, D., Subbarayan, G., and Nguyen, L. (April 15, 2008). "A Nonlinear Fracture Mechanics Approach to Modeling Fatigue Crack Growth in Solder Joints." ASME. J. Electron. Packag. June 2008; 130(2): 021003. https://doi.org/10.1115/1.2840057
Download citation file:
Get Email Alerts
Sequential Versus Concurrent Effects in Combined Stress Solder Joint Reliability
J. Electron. Packag
Anand Model Constants of Sn-Ag-Cu Solders: What Do They Actually Mean?
J. Electron. Packag
Related Articles
Validation of a General Fatigue Life Prediction Methodology for Sn–Ag–Cu Lead-Free Solder Alloy Interconnects
J. Electron. Packag (March,2008)
A Damage-Mechanics-Based Constitutive Model for Solder Joints
J. Electron. Packag (September,2005)
A General Methodology to Predict Fatigue Life in Lead-Free Solder Alloy Interconnects
J. Electron. Packag (March,2009)
Creep-Fatigue Life Evaluation for Sn - 3.5 Ag Solder
J. Eng. Mater. Technol (April,2006)
Related Proceedings Papers
Related Chapters
A Fracture Mechanics Method for an Advanced Evaluation of Inclusions and the Prediction of Fatigue Life of Rolling Element Bearings
Bearing and Transmission Steels Technology
Stress Intensity and Fatigue Crack Growth in a Pressurized, Autofrettaged Thick Cylinder
Fracture Mechanics: Fourteenth Symposium—Volume I: Theory and Analysis
Transition of Part-Through Cracks at Holes into Through-the-Thickness Flaws
Fracture Mechanics: Fifteenth Symposium