The brittle failure assessment for the reactor pressure vessel (RPV) of a pressurized water reactor was revised according to the state of the art. The RPV steel is 22 NiMoCr 37 (A 508 Cl. 2). The expected neutron fluence at the end of license (EOL) after of full operation is . The assessment followed a multibarrier concept to independently prove the exclusion of crack initiation, crack arrest, and exclusion of the load necessary to advance the arrested cracks through the RPV wall. Thermal and structural analyses of the RPV were performed both for the reactor shutdown with postulated upset conditions, as the most severe load case at operation, and for loss of coolant accident (LOCA) conditions. For LOCA transients, a leak size screening of different combinations of cold∕hot leg injection of emergency core cooling was performed, and the leading leak size was determined. A fracture mechanics based assessment was carried out for extended circumferential flaws in the weld joint between the RPV shell and the flange, as well as for axial flaws in the nozzle corner. These flaw geometries postulated at locations of the highest principal stresses and lowest temperatures under the respective transient conditions are representative for the brittle failure assessment of the whole vessel. For a normal operation, the maximum crack driving force takes place at high temperatures preceding the upset conditions. The transient follows a load path decreasing with temperature, producing a warm prestressing effect, which is considered in the assessment. Thus, a large safety margin against crack initiation can be demonstrated. At LOCA, the most severe conditions are determined for postulated cracks in the nozzle corner. Here, applying the constraint modified master curve, which takes account of the low stress triaxiality in the component, the exclusion of crack initiation is proven. Furthermore, two additional safety barriers are proven, the crack arrest after postulated crack initiation well within the allowable depth, as well as the preclusion of the load necessary to advance the arrested crack through the RPV wall.
Skip Nav Destination
e-mail: dieter.siegele@iwm.fraunhofer.de
e-mail: igor.varfolomeyev@iwm.fraunhofer.de
e-mail: gerhard.nagel@eon-energie.com
Article navigation
August 2008
Research Papers
Brittle Failure Assessment of a PWR-RPV for Operating Conditions and Loss of Coolant Accident
Dieter Siegele,
e-mail: dieter.siegele@iwm.fraunhofer.de
Dieter Siegele
Fraunhofer Institute for Mechanics of Materials
, Wöhlerstraße 11, 79108 Freiburg, Germany
Search for other works by this author on:
Igor Varfolomeyev,
e-mail: igor.varfolomeyev@iwm.fraunhofer.de
Igor Varfolomeyev
Fraunhofer Institute for Mechanics of Materials
, Wöhlerstraße 11, 79108 Freiburg, Germany
Search for other works by this author on:
Gerhard Nagel
e-mail: gerhard.nagel@eon-energie.com
Gerhard Nagel
E.ON Nuclear Power GmbH
, Tresckowstraße 5, 30457 Hannover, Germany
Search for other works by this author on:
Dieter Siegele
Fraunhofer Institute for Mechanics of Materials
, Wöhlerstraße 11, 79108 Freiburg, Germanye-mail: dieter.siegele@iwm.fraunhofer.de
Igor Varfolomeyev
Fraunhofer Institute for Mechanics of Materials
, Wöhlerstraße 11, 79108 Freiburg, Germanye-mail: igor.varfolomeyev@iwm.fraunhofer.de
Gerhard Nagel
E.ON Nuclear Power GmbH
, Tresckowstraße 5, 30457 Hannover, Germanye-mail: gerhard.nagel@eon-energie.com
J. Pressure Vessel Technol. Aug 2008, 130(3): 031403 (8 pages)
Published Online: June 6, 2008
Article history
Received:
September 3, 2005
Revised:
May 18, 2007
Published:
June 6, 2008
Citation
Siegele, D., Varfolomeyev, I., and Nagel, G. (June 6, 2008). "Brittle Failure Assessment of a PWR-RPV for Operating Conditions and Loss of Coolant Accident." ASME. J. Pressure Vessel Technol. August 2008; 130(3): 031403. https://doi.org/10.1115/1.2937759
Download citation file:
61
Views
Get Email Alerts
Cited By
Surface Strain Measurement for Non-Intrusive Internal Pressure Evaluation of a Cannon
J. Pressure Vessel Technol (December 2024)
Dynamic Response and Damage Analysis of a Large Steel Tank Impacted by an Explosive Fragment
J. Pressure Vessel Technol (February 2025)
Related Articles
Safety Assessment of Reactor Pressure Vessel Integrity for Loss of Coolant Accident Conditions
J. Pressure Vessel Technol (February,2012)
CFD Tool for Assessment of the Reactor Pressure Vessel Integrity in Pressure Thermal Shock Conditions: Influence of Turbulence Model and Mesh Refinement on the Vessel Thermal Loading During PTS Transient
J. Pressure Vessel Technol (June,2011)
Scaling of Strength of Metal-Composite Joints—Part I: Experimental Investigation
J. Appl. Mech (January,2010)
Deterministic and Probabilistic Fracture Mechanics Analysis for Structural Integrity Assessment of Pressurized Water Reactor Pressure Vessel
J. Pressure Vessel Technol (June,2016)
Related Chapters
Background InformatIon
Guidebook for the Design of ASME Section VIII Pressure Vessels
Openings
Guidebook for the Design of ASME Section VIII Pressure Vessels
Insights and Results of the Shutdown PSA for a German SWR 69 Type Reactor (PSAM-0028)
Proceedings of the Eighth International Conference on Probabilistic Safety Assessment & Management (PSAM)