In this research, the neutron diffraction technique was used to investigate the residual stress distributions in constrained carbon steel welds. Two full penetration welds were studied using (a) the stringer bead and (b) the temper bead weld techniques in 25 mm thick plate. The welds were not post-weld heat treated. The focus of the measurements is on the values of the subsurface and through-thickness strain/stress variation near the middle of the weld and the toe. The experimental results showed that both processes had high residual stresses particularly through the thickness. The measurements were compared with current fitness-for-purpose approaches, such as BS7910 and R6. It was found that the residual stress distribution in the temper bead welded specimen was not as favorable as suspected and post-weld heat treatment should be recommended to reduce residual tensile stresses in this type of steel welds.
Skip Nav Destination
e-mail: anna.paradowska@stfc.ac.uk
Article navigation
October 2010
Research Papers
Comparison of Neutron Diffraction Measurements of Residual Stress of Steel Butt Welds With Current Fitness-for-Purpose Assessments
Anna M. Paradowska,
Anna M. Paradowska
Science and Technology Facility Council, Rutherford Appleton Laboratory,
e-mail: anna.paradowska@stfc.ac.uk
ISIS Facility
, OX11 0QX, UK
Search for other works by this author on:
John W. H. Price,
John W. H. Price
Department of Mechanical Engineering,
Monash University
, Clayton, VIC 3800, Australia
Search for other works by this author on:
Trevor R. Finlayson,
Trevor R. Finlayson
School of Physics,
University of Melbourne
, Melbourne, VIC 3010, Australia
Search for other works by this author on:
Ronald B. Rogge,
Ronald B. Rogge
Chalk River Laboratories,
Canadian Neutron Beam Centre (CNBC)
, ON, K0J 1J0, Canada
Search for other works by this author on:
Ronald L. Donaberger,
Ronald L. Donaberger
Chalk River Laboratories,
Canadian Neutron Beam Centre (CNBC)
, ON, K0J 1J0, Canada
Search for other works by this author on:
Raafat Ibrahim
Raafat Ibrahim
Department of Mechanical Engineering,
Monash University
, Clayton, VIC 3800, Australia
Search for other works by this author on:
Anna M. Paradowska
Science and Technology Facility Council, Rutherford Appleton Laboratory,
ISIS Facility
, OX11 0QX, UKe-mail: anna.paradowska@stfc.ac.uk
John W. H. Price
Department of Mechanical Engineering,
Monash University
, Clayton, VIC 3800, Australia
Trevor R. Finlayson
School of Physics,
University of Melbourne
, Melbourne, VIC 3010, Australia
Ronald B. Rogge
Chalk River Laboratories,
Canadian Neutron Beam Centre (CNBC)
, ON, K0J 1J0, Canada
Ronald L. Donaberger
Chalk River Laboratories,
Canadian Neutron Beam Centre (CNBC)
, ON, K0J 1J0, Canada
Raafat Ibrahim
Department of Mechanical Engineering,
Monash University
, Clayton, VIC 3800, AustraliaJ. Pressure Vessel Technol. Oct 2010, 132(5): 051503 (8 pages)
Published Online: October 1, 2010
Article history
Received:
August 12, 2008
Revised:
September 30, 2009
Published:
October 1, 2010
Citation
Paradowska, A. M., Price, J. W. H., Finlayson, T. R., Rogge, R. B., Donaberger, R. L., and Ibrahim, R. (October 1, 2010). "Comparison of Neutron Diffraction Measurements of Residual Stress of Steel Butt Welds With Current Fitness-for-Purpose Assessments." ASME. J. Pressure Vessel Technol. October 2010; 132(5): 051503. https://doi.org/10.1115/1.4002162
Download citation file:
Get Email Alerts
Cited By
Surface Strain Measurement for Non-Intrusive Internal Pressure Evaluation of a Cannon
J. Pressure Vessel Technol (December 2024)
Dynamic Response and Damage Analysis of a Large Steel Tank Impacted by an Explosive Fragment
J. Pressure Vessel Technol (February 2025)
Related Articles
Erratum: “A Study of Residual Stresses and Microstructure in 2024-T3 Aluminum Friction Stir Butt Welds” [ASME J. Eng. Mater. Technol., 124 , No. 2, pp. 215–222]
J. Eng. Mater. Technol (October,2002)
Residual Stresses Evaluation in Welds and Implications for Design for Pressure Vessel Applications
J. Pressure Vessel Technol (November,2006)
A Study of Residual Stresses and Microstructure in 2024-T3 Aluminum
Friction Stir Butt Welds
J. Eng. Mater. Technol (April,2002)
Neutron Diffraction Evaluation of Residual Stress for Several Welding Arrangements and Comparison With Fitness-for-Purpose Assessments
J. Pressure Vessel Technol (February,2008)
Related Proceedings Papers
Related Chapters
LOW STRAIN CAPACITY GIRTH WELDS OF NEWLY CONSTRUCTED PIPELINES AND MITIGATIVE APPROACHES
Pipeline Integrity Management Under Geohazard Conditions (PIMG)
Historical Overview
History of Line Pipe Manufacturing in North America
Subsection NE—Class MC Components
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes